Sapphire is a single crystal of alumina with hardness >9H, regarded as the second hardest material in nature, second only to diamonds. Sapphire has good light transmission, strong tensile strength, anti-collision resistance, wear resistance, corrosion resistance, high temperature and high pressure resistance, and biocompatibility, which became an ideal substrate material for making semiconductor optoelectronic components. The electrical properties of sapphire make it a substrate material for manufacturing white and blue LED.
Changzhou Haolilai have years of experience in manufacturing high precision sapphire wafer. Besides standard 2 inch, 4 inch, 6 inch, 8 inch wafer, customized sapphire wafer is also available for us. For other dimension, please feel free contact our sales engineer and we will be glad to discuss the availability of dimension options.
Technical Parameters of sapphire wafer
Property | 2 inch | 4 inch | 6 inch | 8inch |
Diameter | 50.8 ± 0.1 mm | 100 ± 0.1 mm | 150 ± 0.1 mm | 200 ± 0.1 mm |
Thickness |
430 ± 25 um or customized |
650 ± 25 um or customized |
1300 ± 25 um or customized |
1300 ± 25 um or customized |
Roughness | Ra ≤ 0.3 nm | Ra ≤ 0.3 nm | Ra ≤ 0.3 nm | Ra ≤ 0.3 nm |
Warp | ≤ 10um | ≤ 10um | ≤ 10um | ≤ 10um |
TTV | ≤3um | ≤3um | ≤3um | ≤ 3 um |
Scratch/Dig. | 20/10 | 20/10 | 20/10 | 20/10 |
Chip | ≤ 0.2 mm | ≤ 0.2 mm | ≤ 0.2 mm | ≤ 0.2 mm |
Polish | DSP (Double Side Polished); SSP(Single Side Polished) | |||
Shape | Round, Flat | |||
Edge Form | Straight, C Chape | |||
Material | Sapphire crystal | |||
Remarks | All specifications above can be customized upon your request |